硫化镉纳米修饰电极的制备及其光电催化应用

以氯化镉和硫代硫酸钠溶液为电解液,应用循环伏安法,直接在氧化铟锡(ITO)导电玻璃表面电沉积制得硫化镉(CdS)纳米粒子.采用扫描电镜(SEM)和紫外一可见吸收光谱对制得的硫化镉的形状、大小、密度进行表征.在电镀液为0.1MCdCl2和0.02MNa2S2O3,电位范围为-0.2V～-0.8V.沉积40圈,温度50℃条件下,制得的CdS纳米粒子大小均匀,分散性好,平均粒径约为60nm,并用制得的ITO/CdS电极研究了对甲基橙溶液(MeO)的光电催化性能.结果表明,光照条件下,电流增加1约62%.     

溶液反应合成制备硫化镉—碳纳米管纳米复合材料

利用溶液中原位反应过程制备以碳纳米管为载体的硫化镉—碳纳米管纳米复合材料。通过水溶液中的氯化镉与硫代乙酰胺进行反应在碳纳米管载体上生成沉积硫化镉粒子。研究结果表明：调整反应温度条件可以控制生成硫化镉粒子的晶型,常温下有利于合成碳纳米管承载的四方相硫化镉纳米复合材料体系,加热条件下有利于合成碳纳米管承载的六方相硫化镉纳米复合材料体系。研究结果对基于纳米硫化镉的纳米复合材料的物性调控技术具有重要指导意义。     

La-TiO2/Al复合薄膜的制备及其光催化性能研究

采用溶胶-凝胶法制备了以铝片为载体的掺杂La的TiO2薄膜.以甲基橙模拟有机污染物,研究了焙烧温度、不同光源、光照时间等对其光催化性能的影响.结果表明,400℃的焙烧温度光催化性能最好.在纳米TiO2中掺杂La进行修饰,当掺杂量为0.7%时其光催化效率有了明显的提高.紫外灯照射2 h后,催化剂对甲基橙的降解率为97.63%,优于可见光.     

SnO2/TiO2/AER复合光催化剂的制备、表征及其光催化性能

以锡酸钠、硫酸钛和氨水为原料,717型阴离子交换树脂(AER)为载体设计合成了SnO2/TiO2/AER复合光催化剂.采用XRD、SEM及EDS分析等对其表面形貌和结构进行表征,并考察其在可见光照射下对甲基橙溶液的光催化性能.结果表明,金红石型SnO2和锐钛矿型TiO2的复合半导体负载于AER上.其中AER的用量为5 g、n(SnO32-)/n(Ti4+)=1∶4、反应温度为100℃时合成的复合光催化剂对甲基橙溶液的脱色率最高,达94.84％;且重复使用10次后仍然超过90％.     

负载纳米TiO_2活性炭催化降解甲基橙的实验探究

文中以活性炭作为载体,用溶胶-凝胶法制备TiO2/活性炭催化剂,利用超声强化TiO2催化降解染料废水中甲基橙.实验结果表明：在实验范围内,二氧化钛在活性炭上的负载率40%～60%、TiO2/活性炭焙烧温度500℃、焙烧时间2.5h、催化剂加入量为0.75-1.0g/L时降解效果最好,随着甲基橙初始浓度增加,降解效率降低.     

碳纳米管/氟碳乳液复合涂层耐腐蚀性能研究

通过超声波分散技术制备了碳纳米管／氟碳乳液复合涂料。并用交流阻抗谱、极化曲线等测量手段研究了涂覆在A3钢片上碳纳米管／氟碳乳液复合涂层的耐腐蚀性能。结果发现添加较少量的碳纳米管就能显著提高氟碳乳液涂层的耐腐蚀性能。质量分数为3％的碳纳米管／氟碳乳液复合涂层具有较高的阻抗值和腐蚀电位（-0．54V）,较低的腐蚀电流密度（大约10^-7.8A／cm^2）,对Q235钢有很好的耐腐蚀效果。     

竹炭负载TiO_2复合材料对甲基橙光催化降解性能

采用溶胶-凝胶法制备了TiO2/竹炭复合材料,研究了复合材料对偶氮染料甲基橙溶液的光降解。结果表明:在自然光照射下,当温度为343 K、复合材料投加量为0.60～1.20 g时,对5～15 mg/L的甲基橙溶液可达到良好的脱色效果;最佳脱色时溶液pH为2.0;复合材料对甲基橙的光催化降解符合反应一级动力学方程。     

纳米TiO_2的合成及其光催化性能研究

用传统的溶胶-凝胶法、改进的溶胶-水热法制备了纳米TiO2和掺杂纳米TiO2,通过对甲基橙有机废水的光催化降解模拟实验,比较不同产品的光催化性能,发现改进的溶胶-水热法优于传统的溶胶-凝胶法,掺杂纳米TiO2优于纯纳米TiO2.     

膨胀石墨负载氮掺杂二氧化钛降解甲基橙的光催化性能

采用溶胶-凝胶法制备了膨胀石墨负载TiO2和负载氮掺杂TiO2（N-TiO2）光催化剂,用XRD和SEM对样品进行表征,并以甲基橙溶液为目标降解物进行光催化性能的评价。结果表明：纳米TiO2可牢固地负载在膨胀石墨表面和层间,当达到吸附平衡后,煅烧温度为500℃条件下制备的膨胀石墨负载N-TiO2光催化剂在加入量为10 g/L、反应时间60 min的条件下,对初始浓度为15 mg/L的甲基橙溶液的降解率达到95.2%。     

碳纳米管作为催化剂载体的应用研究

碳纳米管是材料科学领域研究的热点,在许多方面有吸引人们的应用前景．综述了近年来碳纳米管作为催化剂载体的应用情况．介绍了碳纳米管的结构和性质,重点讨论了碳纳米管分别作为金属、金属氧化物、金属合金及非晶态合金催化剂载体的催化应用效果．     

纳米碳管/二氧化硅复合凝胶玻璃的XPS研究

分别以物理掺杂和化学掺杂的方式,采用溶胶-凝胶法制备了未经表面修饰纳米碳管( CNTs)和经r-氨基丙基三乙氧基硅烷(NH2 (CH2)3Si(OC2H5)3,APTES)修饰纳米碳管的有机改性SiO2复合凝胶玻璃.在此基础上,以X射线光电子能谱(XPS)为表征手段,对所得两种复合凝胶玻璃中SiO2基质和掺杂CNTs的化学状态进行研究.结果表明,掺杂CNTs改变了复合凝胶玻璃中C和O的原子百分比,对SiO2基质的网络结构产生影响,但对SiO2基质的组成未产生显著影响;无论是在物理掺杂还是化学掺杂的有机改性SiO2复合凝胶玻璃中,CNTs与SiO2间均存在一定的Si-C结合键;在CNTs-SiO2复合凝胶玻璃中,以APTES作为桥梁,实现了CNTs与SiO2网络间的化学键合.     

Hydrogenation of ortho-nitrochlorobenzene on activated carbon supported platinum catalysts

INTRODUCTION 2,2′-dichlorohydrazobenzene (DHB) is a com-mercially important intermediate, and is convention-ally manufactured by zinc reduction of or-tho-nitrochlorobenzene (Xu, 1996). The major dis-advantage of this process is the generation of largeamounts of sludge in reduction. A single step catalytichydrogenation of ortho-nitrochlorobenzene to DHBusing supported noble metal catalyst in the presenceof aqueous sodium hydroxide medium becomes moreimportant, because it is enviro…     

碳纳米管在药物载体领域的应用

医学中开发新型药物载体对研究药物具有重要作用,作为一种具有独特纳米管径与中空结构的碳纳米管,可将其纳入药物载体范畴,以核酸、蛋白、药物分子以及肽所修饰的新型碳纳米管为载体,将生物活性分子运载至细胞中,而且不会产生毒性。本研究主要对碳纳米管在药物载体领域的应用进行分析与探讨。     

Synthesis of TiO_2 supported on activated carbon by MOCVD:operation parameters study

A novel metallo-organic chemical vapor deposition (MOCVD) technique has been applied to the preparation of the photocatalytic titanium dioxide supported on activated carbon. The effects of various condition parameters such as carrier gas flow rate, source temperature and deposition temperature on the deposition rate were investigated. The maximum deposition rate of 8.2 mg/(g·h) was obtained under conditions of carrier gas flow rate of 400 ml/min, source temperature of 423 K and deposition temperature of 913 K. The deposition rate followed Arrhenius behavior at temperature of 753 K to 913 K, corresponding to activation energy Ea of 51.09 kJ/mol. TiO2 existed only in anatase phase when the deposition temperature was 773 K to 973 K. With increase of deposition temperature from 1073 K to 1273 K, the rutile content sharply increased from 7% to 70%. It was found that a deposition temperature of 773 K and a higher source temperature of 448 K resulted in finely dispersed TiO2 particles, which were mainly in the     

Synthesis of TiO2 supported on activated carbon by MOCVD:operation parameters study

A novel metallo-organic chemical vapor deposition (MOCVD) technique has been applied to the preparation of the photocatalytic titanium dioxide supported on activated carbon. The effects of various condition parameters such as carrier gas flow rate, source temperature and deposition temperature on the deposition rate were investigated. The maximum deposition rate of 8.2 mg/(g.h) was obtained under conditions of carrier gas flow rate of 400 ml/min, source temperature of 423 K and deposition temperature of 913 K. The deposition rate followed Arrhenius behavior at temperature of 753 K to 913 K, corresponding to activation energy Ea of 51.09 kJ/mol. TiO2 existed only in anatase phase when the deposition temperature was 773 K to 973 K. With increase of deposition temperature from 1073 K to 1273 K, the rutile content sharply increased from 7% to 70%. It was found that a deposition temperature of 773 K and a higher source temperature of 448 K resulted in finely dispersed TiO2 particles, which were mainly in the range of 10-20 nm.     

微波辐射活性炭负载钨硅酸催化合成乙二酸二丁酯

借助微波辐射技术,以活性炭负载钨硅酸为催化剂,以乙二酸和正丁醇为原料合成乙二酸二丁酯.通过正交实验,探讨了诸因素对酯化率的影响,结果表明:活性炭负载钨硅酸具有良好的催化活性,当乙二酸用量为0.05 mol, 醇酸摩尔比为2.6∶ 1,催化剂用量为反应物总质量的8.0 %,微波输出功率为325 W,辐射时间为10 min,带水剂环己烷8 mL,在此优化条件下,反应的酯化率可达96.8 %.该催化剂易于回收且可重复使用,具有价廉易得、催化效果好、操作简单、无环境污染等优点.     

活性炭负载纳米TiO_2光催化降解直接湖蓝实验研究

研究了活性炭负载纳米TiO2的光催化降解性能和直接湖蓝废水处理的主要因素。结果表明:用活性炭负载TiO2具有催化效果好、可重复使用等优点;采用光强为4 050μW/cm2的紫外灯,处理100mg/L直接湖蓝废水的最优工艺条件是:废水pH值为1、光照时间为90min、载体粒径为35～55目。在此条件下,催化剂重复使用16次后对直接湖蓝的去除率为94%。     

活性炭纤维负载纳米TiO_2光催化降解苯实验研究

通过对活性炭(ACF)负载纳米TiO2降解苯的实验研究,分析了TiO2负载量、光照条件、苯初始浓度及ACF/TiO2层数对催化剂活性的影响,结果表明:适量负载TiO2能充分发挥ACF的吸附性和TiO2的光催化功能,提高降解效果;ACF/TiO2在不同光照条件下紫外光效果自然光效果黑暗条件效果;苯初始浓度在一定范围(200ppm)时,18.49g/m2 ACF/TiO2具有良好的降解效果,浓度太高,降解效果不理想;在苯浓度为100ppm的实验环境下,3层ACF/TiO2就足以起到很好的降解效果,因此在设计滤毒罐时,可以根据使用场所有毒气体浓度的不同采用不同层数的ACF/TiO2装填滤毒罐。     

激光轰击制备碳纳米管及其相关纳米材料

采用Nd：YAG脉冲激光在常温常压下轰击浸于乙醇流动相中的铁／石墨混合靶进行制备碳纳米管的研究。用傅立叶红外光谱、X射线衍射和透射电镜等现代分析技术分别对激光轰击所得产物进行表征。结果表明，以铁为催化剂，激光波长为1064nm，激光功率密度为4．5x10^9W/cm^2的条件下可成功制备碳纳米管，并且，透射电镜观察到所得的碳纳米管管径约为20～50nm，长度约几百nm，最长可达1μm以上。