Synthesis of Ag（Nb0.8Ta0.2）O3 Ceramics Under Different Ambient Conditions

Different ambient conditions for the synthesis of Ag（Nb0.8Ta0.2）O3 ceramics were investi- gated. The Ag（Nb0.8Ta0.2）O3 powder was synthesized at 950 ℃ under different ambient conditions, and then pressed into disks and sintered between 1060 ℃ and 1100 ℃ respectively. Samples were investigated by X-ray diffraction, scanning electron microscopy and dielectric measurement. The results show that perovskite Ag（Nb0.8Ta0.2）O3 powder was easier to be synthesized in air than in vacuum at 950℃. Grain size of ceramic samples sintered in air was uniform （about 1 μm） and its dielectric loss was small for its high density. However, the samples decomposed greatly and ceramics could hardly be densified when sintered in vacuum, Thus,. higher atmospheric pressure and oxygen atmosphere would benifit the synthesis of Ag （Nb0.8Ta0.2）O3, and suppress its decomposition at high temperature.     

2001年全国高考化学试题（广东、河南卷）第24题分析

试题：将等物质的量的两种氧化物溶于100mL硫酸，而后逐滴加入1．00mol／L的NaOH溶液。当加入的NaOH的体积V1=50mL时，开始有沉淀析出，且沉淀量随NaOH加入量逐渐增加。当NaOH的体积V2=650mL时，淀淀量达最大值，继续滴加NaOH时，沉淀量逐渐减小。当V3≥750mL时，沉淀量不再改变。     

非金属元素最高价氧化物和气态氢化物的组成

【问题的由来】 我国中学化学的知识内容在一段时期内是以物质结构和元素周期系为主线的。笔者在接触的众多化学习题中，发现许多题目考察了类似SO3和H2S这样的同一非金属元素的最高价氧化物及气态氢化物的有关知识。一般而言，除氢、硼、氧、氟以外的非金属元素（R）在周期表中的族序数为工其最高正价相应为x，最低负价则为（8-x），R元素的最高价氧化物的化学式为R2Ox或ROx/2；气态氢化物的化学式SH（8-x），它们的元素组成具有一定的量的关系。另外，中学生对于用字母代替具体数字的计算往往感到有一定难度。为了揭示这种关系，同时训练学生的抽象思维能力，笔者创作了此习题。     

溶胶-凝胶(Sol-Gel)技术在氧化物纤维中的应用

溶胶-凝胶(Sol-Gel)技术是一种很有发展前途的固体材料制备方法,已引起众多领域重视.简述了溶胶-凝胶技术的发展历史,总结了溶胶-凝胶技术的分类、原料以及无机盐和金属醇盐的水解反应机理,并概括了该技术的优点及存在的问题,着重介绍了溶胶凝胶技术在耐烧蚀陶瓷纤维、高温超导纤维、铁电压电纤维、磁性纤维等氧化物纤维制备方面的应用现状,并对溶胶-凝胶技术的未来发展进行了展望.     

Properties of phosphorus-doped ZnO film deposited by radio-frequency magnetron sputtering

1 Introduction a Zinc Oxide (ZnO), a II-VI compound semiconductor with a wide direct band gap of about 3.4 eV [1], has been extensively studied in recent time for their possible applications in short-wavelength light-emitting devices [2], surface wave dev…     

共沉淀法制备La_(2-x)Sr_xCuO_4及LaSrCu_(1-y)W_yO_4

采用共沉淀法制备钙钛矿氧化物La_(2-x)Sr_xCuO_4及LaSrCu_(1-y)W_yO_4,通过X-射线衍射(XRD)、比表面测定仪(BET)等技术测试钙钛矿样品的晶体结构及比表面积.XRD测试结果表明,对于La_(2-x)Sr_xCuO_4类钙钛矿型氧化物,随着Sr掺杂量的增加,钙钛矿结构的物质杂峰会有所增多;此外,对于LaSrCu_(1-y)W_yO_4而言,W掺杂量对钙钛矿氧化物的晶型结构的影响较小.比表面实验表明,无论是A位元素部分调整还是B位元素部分取代,La_(2-x)Sr_xCuO_4及LaSrCu_(1-y)W_yO_4的比表面积都有明显的增加,但是当比例达到某一值后反而会有所下降。     

药物杂质普卡必利-N-氧化物的结构分析

以4-乙酰氨基-5-氯-2,3-二氢苯并呋喃-7-羧酸甲酯为起始原料,先水解得4-氨基-5-氯-2,3-二氢苯并呋喃-7-羧酸,再将其与1-(3-甲氧基丙基)-4-哌啶胺进行酰胺缩合反应,制得普卡必利-N-氧化物.普卡必利-N-氧化物是一种重要的药物杂质,先用元素分析(EA)和液相色谱-高分辨质谱(LC-HRMS)对普卡必利-N-氧化物的组成进行了化学组分分析,然后采用一维(¹H、1H、⁽¹³⁾C和DEPT)和二维谱((13)C和DEPT)和二维谱(¹H-1H-¹H COSY、1H COSY、¹H-1H-⁽¹³⁾C HSQC和(13)C HSQC和¹H-1H-⁽¹³⁾C HMBC)等多种核磁共振技术对普卡必利-N-氧化物的碳氢信号进行了归属,确定该化合物的准确结构.     

锂离子蓄电池正极材料锂锰氧化物掺杂改性的研究

锂离子蓄电池是21世纪的理想能源。作为LiCoO2的替代材料锰酸锂无论是在价格、环保还是在安全可靠性方面都具有无可比拟的明显的优势。但尖晶石结构锰酸锂，其容量迅速衰减问题至今尚未解决，距离实际应用还有很大差距。当前，层状锰酸锂的研究已受到世界各国的广泛关注。近年来大量研究表明，对锂锰尖晶石进行阳离子或阴离子掺杂以部分取代锰原于或氧原子。可以有效的提高锂锰尖晶石正极材料的循环可逆性。本文重点研究了其电化学特性与有关掺杂改性的机理，并初步探讨了锂锰氧化物的结构、合成及其发展。     

化学式归类解析

1、根据元素质量比判断化学式 例1 在某氮的氧化物中，氮元素与氧元素的质量比为7：16，该氧化物的化学式为（ ）     

LaCoO3复合氧化物纳米材料的制备及其甲醛敏感性能

以柠檬酸为络合剂,采用溶胶-凝胶法制备了具有钙钛矿型结构的稀土复合氧化物LaCoO3纳米材料,借助热重分析（TG）、X-射线衍射（XRD）、透射电子显微镜（TEM）等测试手段对凝胶前驱物和所得纳米材料进行了表征;结果表明,所得LaCoO3纳米材料为沿钙钛矿结构三重轴发生形变而形成的菱方晶系,其产物的平均粒径约为38nm,且颗粒均匀;将所得纳米材料制成气敏元件并测试其气敏性能,结果发现在248℃时LaCoO3纳米材料对甲醛的灵敏度最高为21,且具有较好的选择性（乙醇除外）,通过将来进一步提高对乙醇气体的选择性,该材料很有希望成为一种检测甲醛的敏感材料。