INTRODUCTION Veselago (1968) showed that if both the permit- tivity ε and the magnetic permeability μ of a material are negative, the propagation direction of an elec- tromagnetic (EM) wave will be opposite to its energy flow direction. Such media are called left-handed materials (LHMs) since the electric field E, magnetic field H, and wave vector k in these media form a left-hand triplet of vectors, instead of a right-hand triplet observed in conventional materials. For a long time, …     

热处理时间对IT0薄膜显微组织及光电性能的影响

采用溶胶一凝胶法在玻璃基体上制备了ITO薄膜,研究了后续热处理时间对ITO薄膜显微组织及光电性能的影响。研究结果表明:随着热处理时间的延长,ITO薄膜的微观形貌发生了很大的变化,出现了小丘生长并伴随着回复与再结晶过程,严重影响了ITO薄膜的光电性能。     

DyFeCo磁光薄膜的制备和特性研究

本文采用射频磁控溅射方法制备了ＤｙＦｅＣｏ非晶磁光薄膜，研究了氩气压、溅射功率对ＤｙＦｏＣｏ薄膜性能的影响，实验表明：反射率随惶气压升高而降低，矫顽力随敢压升高而逐渐增大，达到一定值时克尔回线反应，随后矫顽力又逐渐减少，高气压下的矫顽力温度特性较低气压下的矫顽力温度特性要好，但氩气压进一步升高，磁光克尔回线矩形度变差，本征磁光克尔角随氩气压升高而增大，到达最大值后又逐渐减少。反射率随溅射功率增加而     

SiOxNy薄膜退火过程中N元素的流失对于Si结晶的影响

通过不同的溅射工艺制得了3组SiOxNy薄膜样品,并进行了不同的退火工艺。在退火后的样品分析结果中发现了薄膜中的N流失现象,并且对N流失促进了Si结晶的这种特点进行了分析和讨论,为今后利用N流失现象进行S i纳米量子点的制备提供了实验和理论依据。     

《蟾蜍肠系膜血液循环观察》实验的改进

要观察好肠系膜的血液循环，关键在于被观察的肠系膜的完体性及承载场系膜的器材是否能起到良好的实验效果．本文着重解决了这方面的问题。     

衬底状态及热处理对Sm-Fe GMFs磁致伸缩性能的影响

采用IBS法在锡青铜衬底上溅射沉积Sm-Fe非晶态超磁致伸缩薄膜,研究衬底的表面状态和薄膜热处理对Sm-Fe薄膜磁致伸缩性能的影响.实验结果表明,锡青铜衬底状态对Sm-Fe超磁致伸缩薄膜磁伸性能有很大影响.样品经过200℃真空热处理后,100 mT内dλ/dH值从制备态Sm-Fe薄膜的0.71×10-3 T-1提高到2.48×10-3 T-1,薄膜低场磁敏性得到显著提高.     

多功能薄膜干涉实验装置的应用

在常规实验装置的基础上设计安装了一个光具架,由此制成了一种多功能薄膜干涉实验装置。在该装置上不仅可以完成常规的牛顿环实验,还可完成劈尖干涉实验和多种扩展实验,解决了在单一薄膜干涉实验装置上只能完成一种实验的弊端。     

界面量子起伏对铁电超晶格介电性质的影响

应用平均场理论，在横场伊辛模型的框架内，研究了界面量子起伏对铁电超晶格介电性质的影响。得到界面的量子起伏会导致铁电超晶格的介电极化率的升高。     

分形理论及其在薄膜微结构研究中的应用

介绍分形的基本概念以及几种常用的计算简单分形维数的方法,用分形研究Au-MgF2纳米金属介质复合薄膜中Au颗粒和半连续Ag膜中Ag小岛的分布规律。结果表明:复合薄膜中Au颗粒的分形维数随Au含量的增加由1.5516逐渐增大到1.7671,表明金属介质复合薄膜中Au颗粒的平均尺寸随着Au含量的增加而增大;半连续Ag膜中Ag小岛的分形维数随厚度的增加从1.4051增大到1.7428,说明半连续Ag膜的覆盖率随着其厚度的增加而增大。这一结果与实验结果一致,因此分形可以用来定量表征薄膜显微结构的演化规律。