不同形貌氧化锌纳米结构的水热合成、表征和场发射特性

以Zn（NO3）2.6H2O和NaOH为原料,采用改进的水热法通过控制反应溶液的浓度、反应温度和反应时间等沉积参数,合成了包括氧化锌纳米棒阵列、蜂窝状氧化锌纳米棒、花状氧化锌纳米棒等纳米结构.用XRD、SEM和HR-TEM对样品进行了表征,结果表明所制样品为六方纤维锌矿结构的ZnO晶体;SEM测试结果显示ZnO晶体的形貌呈花状和蜂窝棒状等形貌,HR-TEM结果表明单晶纳米棒沿[0001]方向生长.研究了玻璃衬底上装配的花状氧化锌纳米棒的场发射特性,测试结果表明花状氧化锌纳米棒具有优良的场发射;开启场强为4.3V/μm,当场强为8V/μm时,发射电流密度达到2.2mA/cm2.     

硼碳氮纳米管薄膜的制备及场致电子发射性能研究

采用高温热解法,以硼氢化纳/乙二胺(NaBH4/C2H8N2)饱和溶液为前驱液在沉积有铁催化剂的硅基底上生长硼碳氮(BCN)纳米管.利用扫描电子显微镜、高分辨率透射电子显微镜、扫描俄歇微探针和拉曼光谱对BCN纳米管进行形貌观察和表征.BCN纳米管的高度在20μm左右,直径在50～100nm之间,具有明显的"竹节状"结构,结晶有序度较差.对BCN纳米管薄膜进行低场致电子发射性能测试,开启电场1.8V/μm,外电场升至2.48V/μm时发射电流170μA/cm2,当外加电场大于5.5V/μm时,可以观察到发射点均匀分布的场致电子发射图像.     

Hf_(0.5)Zr_(0.5)O_2铁电薄膜的制备和性能研究

运用脉冲激光沉积方法,在Pt(111)基片上沉积制备Hf0.5Zr0.5O2铁电薄膜。通过对X射线衍射(XRD)分析表明,薄膜的正交相随衬底温度升高而增强,随薄膜厚度增加而减小。P-E电滞回线实验表明,提高衬底温度有助于增强薄膜铁电性能。400℃氧气中原位退火后薄膜剩余极化(2Pr)达到8μC/cm2。5V以下薄膜漏电流密度为3.2×10-6A/cm2。Hf0.5Zr0.5O2薄膜的疲劳特性测试表明,在经过2×109次反转后可参与翻转总极化值有一定下降。     

纳米石墨烯微通道板的场发射特性

纳米石墨烯丰富的尖端和缺陷能够提高材料的场发射性能.然而其与衬底的粘附性差导致在场发射过程中容易发生真空间隙击穿,引起器件失效.本文采用新颖的溶剂热渗碳方法制备了纳米石墨烯包覆硅微通道板,形成石墨烯微通道板(MLG-MCPs).纳米石墨烯的表面形貌和晶体机构由Raman和TEM进行表征,MLG横向尺寸50～100 nm,呈涟漪和褶皱形状,具有较高的结晶度.场发射测试结果显示800℃退火能增加缺陷密度,降低功函数,开启电场降至2.0 V/μm(10μA/cm~2),显示了较好的场发射特性.     

用旋转喷镀法制备Ni-Zn-Co铁氧体薄膜

用旋转喷镀法制备Ni–Zn–Co铁氧体薄膜。通过FeCl2 NiCl2 ZnCl2 CoCl2组成的还原液和CH3COONH4 NH3H2O NaNO2组成的氧化液不断地向转盘上的玻璃基片喷镀,在90℃下反应制备了厚度1–2μm的Ni–Zn–Co铁氧体薄膜。利用X射线衍射(XRD)确定样品的物相,用扫描电子显微镜(SEM)观察分析了薄膜的形貌,用振动样品磁强计(VSM)和矢量网络分析仪测量了薄膜的磁性能。     

含氮氟化非晶碳（a-C：F：N）薄膜电学性能的研究

用射频等离子体增强化学气相沉积（RF-PECVD）法制备氮掺杂氟化非晶碳（a-C：F）薄膜，用电桥测试薄膜的介电常数．研究不同工艺参量对薄膜电学性能的影响．结果表明：掺杂氮、高射频功率、高沉积温度以及热退火都导致薄膜介电常数上升．     

掺碳氧化锌薄膜的铁磁性

采用磁控溅射方法在Al2O3（0001）和Si（100）衬底上制备掺碳氧化锌薄膜,溅射薄膜时衬底温度为550°C.实验结果显示,制备的掺碳氧化锌薄膜样品在Al2O3（0001）单晶衬底上结晶质量更好.在室温下,所制备的薄膜皆出现铁磁性,且在Si（100）衬底上制备的样品具有更大的饱和磁化值.实验结果表明氧空位缺陷对掺碳氧化锌薄膜的铁磁性起源有很重要的影响.     

氧化锡纳米线在场致发射显示器中的应用研究

采用改进的热蒸发法制备了大量的一维氧化锡纳米线,利用丝网印刷工艺将制备的氧化锡纳米线印刷在玻璃基板银电极上作为场发射阴极材料,研究了阴极的场致发射特性,实现了原型显示器件的均匀点亮,实验结果表明,该方法制备的氧化锡纳米线作为阴极材料具有低的阈值电场(6.67 V/μm)、高的发射电流密度(205μA/cm2)和好的场发射稳定性(发射电流涨落幅度在10%以内).     

氢化非晶碳膜导电机制的探索

采用电子回旋共振等离子离子体化学气相沉积（ＥＣＲ－ＣＶＤ）方法，以苯为气源，在不同基片温度下制备了氢化非晶碳膜（ａ－Ｃ：Ｈ），对样品进行了伏安特性测试，考察了基片温度对样品电阻率与击穿场强的影响，结合薄膜含氢量，ＳＥＭ、Ｒａｍａｎ散射等分析手段探索了ａ－Ｃ：Ｈ膜的导电机制。     

TiO_2修饰层与ZnO复合薄膜中非晶化现象研究

为改善ZnO薄膜的光学性质,采用溶胶-凝胶法分别制备了3层和6层ZnO基底上覆不同层数TiO_2修饰层的透明薄膜,分析TiO_2修饰层对薄膜晶体结构的影响。用不同工艺流程制备了覆TiO_2修饰层的ZnO基透明薄膜,研究非晶化出现的过程。结果表明:所有混合镀膜样品,其结晶性均受到阻碍,所得样品呈现出明显的非晶状态;非晶化的出现会对薄膜的光学性质产生显著影响。非晶化过程发生在样品制备过程中的预处理和退火阶段,其中退火过程中的非晶化更为主要。     

二氧化钛薄膜光催化降解次甲基兰

采用溶胶-凝胶法在玻璃表面制得TiO2薄膜,研究以365 nm的紫外光为光源,次甲基兰在TiO2薄膜上的光催化降解效果与光照时间、镀膜层数的关系,以及膜的重复利用次数.实验表明:4层TiO2薄膜在光照4 h时光催化降解率达到95.9%.     

静态箱法在甲烷排放及稻田甲烷减排策略研究中的应用

为揭示天然湿地与稻田甲烷排放特征的差异,采用静态箱法对闽江河口天然湿地和稻田甲烷排放特征进行了比较,并探讨了水旱轮作的甲烷减排模式。结果表明:早稻田平均甲烷排放量为17.03 mg/m2.h,高于相应季节的天然芦苇沼泽甲烷排放量(7.47 mg/m2.h);天然湿地和稻田土壤理化特征差异是导致甲烷排放量不同的主要原因;早稻田甲烷排放量日变化主要受温度影响,而潮汐是影响天然芦苇沼泽的关键因素;水旱轮作可有效降低稻田甲烷排放。     

光学发射谱在硫掺杂金刚石薄膜制备中的应用

利用辉光等离子体辅助热丝化学气相沉积法,制备硫掺杂n型金刚石薄膜,利用光学发射谱技术对其生长环境进行原位诊断,分析合成机理及生长的最佳条件。结果表明,合成金刚石薄膜的合成反应区中主要粒子为CH、CH+、活性H原子,提高工作气压和硫碳配比浓度有利于提高硫掺杂浓度,在低温条件下合成了高品质的硫掺杂n型金刚石薄膜。     

氩氧比对射频反应磁控溅射制备TiO2薄膜亲水性能的影响

采用射频磁控溅射法制备了锐钛矿相TiO2薄膜,在基片温度、溅射功率、溅射时间以及靶材与基片间的距离等因素不变的情况下,研究不同氩氧分压比对薄膜亲水性能的影响。通过原子力显微镜(AFM)、X射线衍射光谱(XRD)表征了薄膜的微观表面形貌和晶相组成,采用静态接触角(SCA)评估薄膜的亲水性。实验结果表明不同氩氧比制备的锐钛矿相TiO2薄膜,紫外光照12 h后,接触角降到10o左右,而氩氧比小于等于5:5的接触角都低至5o左右,达到了超亲水性。氩氧分压比为4:6时,样品薄膜的光致亲水性最佳且光照后亲水性的保持较长。     

脉冲激光沉积法在多孔硅衬底上制备ZnS薄膜

用电化学阳极氧化法制备了一定孔隙率的多孔硅样品,然后用脉冲激光沉积法以PS为衬底生长一层ZnS薄膜.用X射线衍射仪、扫描电子显微镜和荧光分光光度计分别表征了ZnS薄膜的结构、形貌和ZnS/PS复合膜的光致发光性质.XRD结果表明,制备的ZnS薄膜沿β-ZnS(111)方向择优生长,结晶质量良好,但衍射峰的半峰全宽较大;SEM图像显示,ZnS薄膜表面出现一些凹坑,这是衬底PS的表面粗糙所致.室温下的光致发光谱表明,沉积ZnS薄膜后,PS的发光峰蓝移.把ZnS的蓝绿光与PS的橙红光叠加,在可见光区450~700 nm形成了一个较宽的光致发光谱带,ZnS/PS复合膜呈现较强的白光发射.     

Characteristics of fluoride emission from five clay minerals as affected by temperature, heating time and addition of calcium compounds

Characteristics of fluoride emission from five clay minerals (montmorillonite, kaolinite, vermiculite, geothite, and allophane) as affected by temperature, heating time and addition of calcium compounds were studied. Marked increase of the fluoride emission rate was noticed with increase of temperature. The fluoride release, began at 500°C–600°C, and the main bulk of the fluoride emission occurred at the temperature of about 800°C. The loss of crystalline water was primarily responsible for the increase of fluoride emission. When minerals were heated at 800°C, The fluoride emission rate from the clay minerals reached the highest after heating for 1 hour. The samples treated by CaO, CaCO₃, Ca(OH)₂, Ca₃(PO₄)₂, and CaSO₄ had 55.45%, 59.58%, 46.45%, 54.31%, 31.25% reduction in the fluoride emission from montmorillonite at the temperature of 800°C, respectively. CaCO₃ had the highest fluoride fixing capacity compared to other calcium compounds. Project supported by the Special Funds for Major State Basic Research Project 973 (G1999011809) and Natural Science Foundation of Zhejiang Province.     

两优6326作再生稻在豫南稻区的种植表现及高产栽培技术

为提高豫南稻区自然资源利用率,获得高产栽培技术,试验选用早熟、再生能力强的水稻品种两优6326,采用提前播种、覆膜畦厢式健身栽培的种植方式,以覆膜、不覆膜Ⅱ优838为对照,从特征特性及产量表现上进行试验分析.结果证明：两优6326作为再生稻种植,其产量前季可达641.6 kg/667m2,再生季可达178.8 kg/667m2,适合在豫南稻区作再生稻种植.     

Modeling and analysis of wet clutch engagement characteristics

A mathematical model was developed to analyze the characteristics of the wet clutch during engagement. The lubricant squeeze action was simulated with Patir and Cheng average flow model in which the permeability of friction material is taken into account, and the asperity load is calculated according to the Greenwood and Tripp approach. In this model, effects of friction material permeability, applied load and driving velocity on the engagement characteristics of the wet clutch were studied. The results show that friction material with high permeability reduces the film thickness rapidly and increases the torque peak; the applied load increases the asperity contact pressure and the friction torque, and reduces the engagement time; the driving velocity mainly increases the engagement time. The theoretical torque and relative velocity curves agree qualitatively with the experimental ones, which verifies the wet clutch engagement model.     

明胶-葡甘聚糖-聚乙烯醇肥料包膜的制备及性能

以甲醛作交联剂,甘油为增塑剂,用溶液共混法制备了明胶-葡甘聚糖-聚乙烯醇缓释肥料包膜．测定了包膜的吸水率、拉伸强度和断裂伸长率,考察了明胶、葡甘聚糖、聚乙烯醇的质量比,甲醛、甘油用量对包膜的耐水性能和力学性能的影响,同时研究了包膜中尿素的释放性能．结果表明：在50℃下,当甲醛用量为5ml,甘油用量为0．5ml,明胶、葡甘聚糖、聚乙烯醇的质量比为4：3：3时,制备出的包膜综合性能较好,膜中尿素有良好的缓释性能．该条件下包膜中原料之间产生了较强的相互作用,形成了一个较稳定的复合体,且具有良好的缓释性能．     

基于产业集中度的中国电影产业集聚研究

近年来,我国文化产业改革力度不断加大,电影产业和电影经济持续蓬勃发展。然而,目前对中国电影经济的时空集聚和演变的研究仍然不多。利用产业经济学的方法,对我国的电影经济的时空集聚和演变进行了探索性的研究。结果表明:我国电影产业在省级区域层面整体具有一定的集中度,市场竞争不是特别激烈,市场结构整体属于寡占Ⅳ型;我国电影产业在市域层面的整体的集中度有限,市场竞争特征较为明显,市场结构基本属于低集中竞争型;我国电影院线具有一定的行业集中度,在某些方面也存在竞争特点,寡占Ⅳ型居多;我国月度电影经济呈现一定的行业集中度,整体市场结构属于寡占Ⅳ型;档期电影经济呈现很高的行业集中度,整体市场结构属于寡占型中的最高级别;我国电影经济的产业集中度特征较明显,呈现出“省域和市域市场结构有差异,企业和时间层面均呈寡占”的特点。